Olefin
|
PROPERTIES |
ASTM TEST METHOD |
UNITS |
GENERAL
PURPOSE |
GLASS
REINFORCED |
|
||
|
|
|
|
|
35% |
|
||
|
|
|
|
ZS-10ZS-30 |
ZR-17 ZR-37 |
|
||
|
MECHANICAL |
|
|
|
|
|
||
|
Tensile
Strength Ultimate
Elongation Flexural
Modulus of Elasticity Flexural
Strength Izod Impact
Strength 1/8” Thickness Notched @ 73F (23C) Rockwell
Hardness Compressive
Strength at Yield |
D-638 D-638 D-790 D-790 D-256 D-785 D-695 |
psi MPa % psi MPa psi MPa ftlb/in J/m M Scale R Scale psi MPa |
7,400 51 50 275,000 1900 9,500 65 1.5 80 70 112 6,600 46 |
20,000 138 6 1,100.,000 7580 28,000 193 2.3 123 88 120 22,000 152 |
|
|
|
|
THERMAL |
|
|
|
|
|
||
|
Melting Range Heat
Deflection Temperature @264 psi @1.82 MPa @66 psi @0.45 MPa |
D-789 D-648 D-648 |
F C F C F C |
410-430 210-221 120 49 320 160 |
410-430 210-221 316 158 350 177 |
|
|
|
|
MISCELLANEOUS |
|
|
|
|
|
||
|
Flammability Moisture Absorption 24 Hour Immersion Specific
Gravity Mold Shrinkage |
UL-94 D-570 D-792 D-955 |
- % - % |
94 HB 0.6 1.05 1.7 – 1.9 |
94 HB 0.4 1.32 0.2 – 0.3 |
|
|
|
Olefin