Glass Fiber Reinforced 6,6
|
PROPERTIES |
ASTM TEST METHOD |
UNITS |
GLASS REINFORCED |
GLASS REINFORCED SUPERIOR FINISH |
|
||||||
|
|
|
|
13% |
20% |
33% |
40% |
33% |
|
|||
|
|
|
|
AR-13AR-33 |
AR-14AR-34 |
AR-17AR-37 |
AR-18 AR-38 |
AW-17 AW-37 |
|
|
|
|
|
MECHANICAL |
|
|
|
|
|
|
|
|
|||
|
Tensile
Strength Ultimate
Elongation Flexural
Modulus of Elasticity Flexural
Strength Izod
Impact Strength 1/8” Thickness Notched @ 73F (23C) Rockwell
Hardness Compressive
Strength at Yield |
D-638 D-638 D-790 D-790 D-256 D-785 D-695 |
psi MPa % psi MPa psi MPa ftlb/in J/m M Scale R Scale psi MPa |
15,500 107 3-4 700,000 4826 25,000 172 0.9 48 95 120 26,000 179 |
18,000 124 3-4 1,100,000 7584 31,000 214 1.4 75 96 121 30,000 207 |
27,000 186 3-4 1,300,000 8964 38,500 265 2.1 112 98 122 35,500 245 |
32,000 221 3-4 1,600,000 11030 42,000 290 2.5 133 101 123 40,000 276 |
27,000 186 3-4 1,300,000 8964 38,000 262 2.2 117 96 121 32,000 221 |
|
|
|
|
|
THERMAL |
|
|
|
|
|
|
|
|
|||
|
Melting
Range Heat
Deflection Temperature @264 psi @1.82 MPa @66 psi @0.45 MPa |
D-789 D-648 D-648 |
F C F C F C |
490-520 254-271 440 227 460 238 |
490-520 254-271 475 246 >480 >249 |
490-520 254-271 480 249 >480 >249 |
490-520 254-271 >480 >249 >480 >249 |
470-490 243-254 455 235 473 245 |
|
|
|
|
|
MISCELLANEOUS |
|
|
|
|
|
|
|
|
|||
|
Flammability Moisture
Absorption 24 Hour Immersion Specific
Gravity Mold
Shrinkage |
UL-94 D-570 D-792 D-955 |
- % - % |
94 HB 1.0 1.22-1.24 0.4-0.7 |
94 HB 0.9 1.28-1.30 0.3-0.6 |
94 HB 0.7 1.38-1.40 0.2-0.5 |
94 HB 0.6 1.46-1.48 01.-0.4 |
94 HB 0.8 1.37-1.38 0.2-0.5 |
|
|
||
|
PROPERTIES |
ASTM TEST METHOD |
UNITS |
MINERAL FILLED |
GLASS REINFORCED MINERAL FILLED |
|
|
|
|
40% |
40% |
|
|
|
|
AH-18AH-38 |
AL-18AL-38 |
|
MECHANICAL |
|
|
|
|
|
Tensile Strength Ultimate Elongation Flexural Modulus of Elasticity Flexural Strength Izod Impact Strength 1/8” Thickness Notched @ 73F (23C) Rockwell Hardness Compressive Strength at Yield |
D-638 D-638 D-790 D-790 D-256 D-785 D-695 |
psi MPa % psi MPa psi MPa ftlb/in J/m M Scale R Scale psi MPa |
13,000 89.6 10-15 900,000 6206 20,000 138 0.7 37 95 122 36,500 252 |
20,000 138 2-3 1,100,000 7584 28,000 193 0.8 43 98 122 37,000 255 |
|
THERMAL |
|
|
|
|
|
Melting Range Heat Deflection Temperature @264 psi @1.82 MPa @66 psi @0.45 MPa |
D-789 D-648 D-648 |
F C F C F C |
490-510 254-266 340 171 410 210 |
490-520 254-271 475 246 480 249 |
|
MISCELLANEOUS |
|
|
|
|
|
Flammability Moisture Absorption 24 Hour Immersion Specific Gravity Mold Shrinkage |
UL-94 D-570 D-792 D-955 |
- % - % |
94 HB 0.6 1.48-1.50 0.9-1.2 |
94 HB 0.6 1.47-1.49 0.4-0.7 |
|
|
|
|
|
|
General Purpose and Impact Modified
|
PROPERTIES |
ASTM TEST METHOD |
UNITS |
GENERAL PURPOSE |
IMPACT MODIFIED |
ULTRA HIGH IMPACT |
|
|
|
|
|
|
|
|
|
|
|
AS-10 AS-30 |
AI-10 AI-30 |
AD-10 AD-30 |
|
MECHANICAL |
|
|
|
|
|
|
Tensile
Strength Ultimate
Elongation Flexural
Modulus of Elasticity Flexural
Strength Izod
Impact Strength 1/8” Thickness Notched @ 73F (23C) Rockwell
Hardness Compressive
Strength at Yield |
D-638 D-638 D-790 D-790 D-256 D-785 D-695 |
psi MPa % psi MPa psi MPa ftlb/in J/m M Scale R Scale psi MPa |
11,800 81.4 50 410,000 2827 16,500 114 1.0 53 79 120 14,000 97 |
8,800 60.7 60 280,000 1931 12,500 86 3.2 171 70 112 11,000 76 |
7,600 52.4 65 264,000 1820 10,400 72 16 854 64 111 9,500 66 |
|
THERMAL |
|
|
|
|
|
|
Melting
Range Heat
Deflection Temperature @264 psi @1.82 MPa @66 psi @0.45 MPa |
D-789 D-648 D-648 |
F C F C F C |
490-510 254-266 172 78 380 193 |
480-500 249-260 158 70 350 177 |
480-500 249-260 158 70 420 216 |
|
MISCELLANEOUS |
|
|
|
|
|
|
Flammability Moisture
Absorption 24 Hour Immersion Specific
Gravity Mold
Shrinkage |
UL-94 D-570 D-792 D-955 |
- % - % |
94 V-2 1.2 1.13-1.15 1.5-1.7 |
94 HB 1.1 1.08-1.10 1.1-1.4 |
94 HB 1.1 1.07-1.09 1.3-1.6 |
|
|
|
|
|
|
|
Glass Reinforced Impact Modified
|
PROPERTIES |
ASTM TEST METHOD |
UNITS |
GLASS REINFORCED IMPACT MODIFIED |
GLASS REINFORCED HIGH IMPACT |
||||
|
|
|
|
13% |
20% |
33% |
13% |
20% |
33% |
|
|
|
|
AT-13AT-33 |
AT-14AT-34 |
AT-17AT-37 |
AJ-13 AJ-33 |
AJ-14 AJ-34 |
AJ-17 AJ-37 |
|
MECHANICAL |
|
|
|
|
|
|
|
|
|
Tensile
Strength Ultimate
Elongation Flexural
Modulus of Elasticity Flexural
Strength Izod
Impact Strength 1/8” Thickness Notched @ 73F (23C) Rockwell
Hardness Compressive
Strength at Yield |
D-638 D-638 D-790 D-790 D-256 D-785 D-695 |
psi MPa % psi MPa psi MPa ftlb/in J/m M Scale R Scale psi MPa |
14,000 96.5 3-4 650,000 4482 21,000 145 2.0 107 84 119 18,000 124 |
16,000 110 3-4 800,000 5516 24,000 165 2.2 117 89 120 22,000 152 |
22,000 152 3-4 1,000,000 6895 33,000 228 2.5 133 95 121 26,000 179 |
13,000 89.6 3-4 550,000 3792 17,600 121 2.8 149 81 118 16,000 110 |
16,000 110 3-4 800,000 5516 21,000 145 3.3 176 85 119 20,000 138 |
21,000 145 3-4 980,000 6757 29,500 203 4.0 213 90 120 23000 159 |
|
THERMAL |
|
|
|
|
|
|
|
|
|
Melting
Range Heat
Deflection Temperature @264 psi @1.82 MPa @66 psi @0.45 MPa |
D-789 D-648 D-648 |
F C F C F C |
480-500 249-260 430 221 445 229 |
480-500 249-260 460 238 480 249 |
480-500 249-260 475 246 >480 >249 |
480-500 249-260 430 221 445 229 |
480-500 249-260 460 238 480 249 |
480-500 249-260 475 246 >480 >249 |
|
MISCELLANEOUS |
|
|
|
|
|
|
|
|
|
Flammability Moisture
Absorption 24 Hour Immersion Specific
Gravity Mold
Shrinkage |
UL-94 D-570 D-792 D-955 |
- % - % |
94 HB 0.8 1.18-1.20 0.6-0.9 |
94 HB 0.6 1.25-1.27 0.4-0.7 |
94 HB 0.5 1.34-1.36 0.2-0.5 |
94 HB 0.8 1.17-1.19 0.6-0.9 |
94 HB 0.6 1.23-1.25 0.4-0.7 |
94 HB 0.5 1.32-1.34 0.2-0.5 |