Nylon 6,6

PROPERTIES	ASTM TEST METHOD	UNITS	GENERAL PURPOSE	IMPACT MODIFIED	ULTRA HIGH IMPACT	GLASS REINFORCED
GLASS/MINERAL CONTENT						15%	20%	35%	40%
PRODUCT			AS-10 AS-30	AI-10 AI-30	AD-10 AD-30	AR-13 AR-33	AR-14 AR-34	AR-17 AR-37	AR-18 AR-38
MECHANICAL
TENSILE STRENGTH	D-638	psi MPa	11,800 81.4	8,800 60.7	7,600 52.4	15,500 107	18,000 124	27,000 186	32,000 221
ULTIMATE ELONGATION	D-638	%	40	60	65	3-4	3-4	3-4	3-4
FLEXURAL MODULUS OF ELASTICITY	D-790	psi MPa	420,000 2896	280,000 1931	264,000 1820	700,000 4826	1,100,000 7584	1,300,000 8964	1,600,000 11030
FLEXURAL STRENGTH	D-790	psi MPa	16,500 114	12,500 86	10,400 72	25,000 172	31,000 214	38,500 265	42,000 290
IZOD IMPACT STRENGTH 1/8" THICKNESS @73F	D-256	ftlb/in J/m	0.9 48	3.2 171	16 854	0.85 45	1.4 75	2.1 112	2.5 133
ROCKWELL HARDNESS	D-785	M Scale R Scale	79 120	70 112	64 111	95 120	96 121	98 122	101 123
COMPRESSIVE STRENGTH AT YIELD	D-695	psi MPa	14,000 97	11,000 76	9,500 66	26,000 179	30,000 207	35,500 245	40,000 276
THERMAL
MELTING RANGE	D-789	F C	490-510 254-266	480-500 249-260	480-500 249-260	490-520 254-271	490-520 254-271	490-520 254-271	490-520 254-271
HEAT DEFLECTION TEMPERATURE @264 @1.82 MPa @66psi @0.45 MPa	D-648 D-648	F C F C	172 78 380 193	158 70 350 177	158 70 420 216	440 227 460 238	475 246 >480 >249	480 149 >480 >249	>480 >249 >480 >249
MISCELLANEOUS
FLAMMABILITY	UL-94		94 V-2	94 HB	94 HB	94 HB	94 HB	94 HB	94 HB
MOISTURE ABSORPTION 24HR IMMERSION	D-570	%	1.5	1.2	1.2	1.0	0.9	0.8	0.6
SPECIFIC GRAVITY	D-792		1.13-1.15	1.08-1.10	1.07-1.09	1.22-1.24	1.28-1.30	1.38-1.40	1.46-1.48
MOLD SHRINKAGE	D-955	%	1.6-1.9	1.1-1.4	1.3-1.6	0.4-0.7	0.3-0.6	.02-0.5	0.1-0.4

PROPERTIES	ASTM TEST METHOD	UNITS	GLASS REINFORCED SUPERIOR FININSH	GLASS REINFORCED IMPACT MODIFIED			GLASS REINFORCED HIGH IMPACT			GLASS REINFORCED MINERAL FILLED	MINERAL FILLED
GLASS/MINERAL CONTENT			35%	15%	20%	35%	15%	20%	35%	40%	40%
PRODUCT			AW-17 AW-37	AT-13 AT-33	AT-14 AT-34	AT-17 AT-37	AJ-13 AJ-33	AJ-14 AJ-34	AJ-17 AJ-37	AL-18 AL-38	AH-18 AH-38
MECHANICAL
TENSILE STRENGTH	D-638	psi MPa	27,000 186	14,000 96.5	16,000 110	22,000 152	13,000 89.69	16,000 110	21,000 145	20,000 138	13,000 89.6
ULTIMATE ELONGATION	D-638	%	3-4	3-4	3-4	3-4	3-4	3-4	3-4	2-3	10-15
FLEXURAL MODULUS OF ELASTICITY	D-790	psi MPa	1,280,000 8826	650,000 4482	800,000 5516	1,000,000 6895	550,000 3792	500,000 5516	950,000 6550	1,100,000 7584	900,000 6206
FLEXURAL STRENGTH	D-790	psi MPa	38,000 262	20,000 138	24,000 165	32,000 221	17,600 121	21,000 145	29,000 200	28,000 193	20,000 138
IZOD IMPACT STRENGTH 1/8" THICKNESS @73F	D-256	ftlb/in J/m	2.3 123	2.0 107	2.2 117	2.5 133	2.4 128	3.1 165	3.8 203	0.6 32	0.8 43
ROCKWELL HARDNESS	D-785	M Scale R Scale	96 121	84 119	89 120	95 121	81 118	85 119	90 120	98 122	95 122
COMPRESSIVE STRENGTH AT YIELD	D-695	psi MPa	32,000 221	18,000 124	22,000 152	26,000 179	16,000 110	20,000 138	23,000 159	37,000 255	36,500 252
THERMAL
MELTING RANGE	D-789	F C	428 220	480-500 249-260	480-500 249-260	480-500 249-260	480-500 249-260	480-500 249-260	480-500 249-260	490-520 254-271	490-510 254-266
HEAT DEFLECTION TEMPERATURE @264 @1.82 MPa @66psi @0.45 MPa	D-648 D-648	F C F C	428 220 473 245	420 216 445 229	461 238 480 249	475 246 480 249	420 216 440 227	435 224 460 238	475 246 480 249	475 246 480 249	340 171 410 210
MISCELLANEOUS
FLAMMABILITY	UL-94		94 HB	94 HB	94 HB	94 HB	94 HB	94 HB	94 HB	94 HB	94 HB
MOISTURE ABSORPTION 24HR IMMERSION	D-570	%	0.8	0.5	0.5	0.5	0.5	0.5	0.5	0.6	0.7
SPECIFIC GRAVITY	D-792		1.37-1.38	1.18-1.20	1.25-1.27	1.34-1.36	1.19-1.21	1.23-1.25	1.31-1.33	1.46-1.48	1.46-1.48
MOLD SHRINKAGE	D-955	%	0.2-0.5	0.6-0.9	0.4-0.7	0.2-0.5	0.6-0.9	0.4-0.7	0.2-0.5	0.4-0.7	0.9-1.2