Glass Reinforced 6

 

 

 

PROPERTIES

 

 

 

ASTM

TEST

METHOD

 

 

 

UNITS

 

 

GLASS

REINFORCED

GLASS

REINFORCED

SUPERIOR

FINISH

 

 

 

13%

20%

33%

40%

33%

 

 

 

BR-13

BR-33

BR-14

BR-34

BR-17

BR-37

BR-18

BR-38

BW-17

BW-37

MECHANICAL

 

 

 

 

 

 

 

 

Tensile Strength

 

 

Ultimate Elongation

 

 

Flexural Modulus

 of Elasticity

 

Flexural Strength

 

 

Izod Impact Strength

  1/8” Thickness        

   Notched

   @ 73F (23C)

 

 

Rockwell Hardness

 

 

Compressive Strength

   at Yield

 

 

 

D-638

 

 

D-638

 

 

D-790

 

 

D-790

 

 

 

 

D-256

 

 

 

 

D-785

 

 

 

D-695

 

 

 

Psi

Mpa

 

%

 

 

psi

Mpa

 

Psi

Mpa

 

 

 

ftlb/in

J/m

 

 

 

M Scale

R Scale

 

 

Psi

Mpa

 

14,500

100

 

4-5

 

 

700,000

4826

 

20,000

138

 

 

 

0.9

48

 

 

 

88

119

 

 

15,000

103

 

17,000

117

 

3-4

 

 

900,000

6206

 

22,000

152

 

 

 

1.5

80

 

 

 

89

120

 

 

20,000

138

 

23,000

159

 

2-3

 

 

1,250,000

8619

 

29,000

200

 

 

 

2.1

112

 

 

 

90

121

 

 

25,000

172

 

 

26,000

179

 

2-3

 

 

1,400,000

9653

 

33,000

228

 

 

 

2.5

133

 

 

 

92

122

 

 

30,000

207

 

22,000

152

 

3-4

 

 

1,200,000

8274

 

28,000

193

 

 

 

2.2

117

 

 

 

89

120

 

 

24,000

165

THERMAL

 

 

 

 

 

 

 

 

Melting Range

 

Heat Deflection

  Temperature

   @264 psi

   @1.82 MPa

 

   @66 psi

   @0.45 MPa

 

D-789

 

 

 

D-648

 

 

D-648

 

F

C

 

 

F

C

 

F

C

 

420-440

216-227

 

 

380

193

 

410

210

 

420-440

216-227

 

 

400

204

 

420

216

 

420-440

216-227

 

 

420

216

 

425

218

 

420-440

216-227

 

 

420

216

 

425

218

 

410-430

210-221

 

 

400

204

 

420

216

MISCELLANEOUS

 

 

 

 

 

 

 

 

Flammability

 

 

Moisture Absorption

  24 Hour Immersion

 

 

Specific Gravity

 

 

Mold Shrinkage

 

UL-94

 

 

 

D-570

 

 

D-792

 

 

D-955

 

-

 

 

 

%

 

 

-

 

 

%

 

 

94 HB

 

 

 

1.5

 

 

1.21 – 1.23

 

 

0.4 – 0.7

 

94 HB

 

 

 

1.2

 

 

1.27 – 1.29

 

 

0.3 – 0.6

 

94 HB

 

 

 

1.1

 

 

1.37 – 1.39

 

 

0.2 – 0.5

 

94 HB

 

 

 

1.0

 

 

1.45 – 1.47

 

 

0.1 – 0.4

 

94 HB

 

 

 

1.1

 

 

1.36 – 1.37

 

 

0.2 – 0.4

 

 

 

 

Glass Reinforced Impact Modified

 

PROPERTIES

 

 

ASTM

TEST

METHOD

 

 

UNITS

GLASS

REINFORCED

IMPACT

MODIFIED

GLASS

REINFORCED

HIGH

IMPACT

 

 

 

13%

20%

33%

13%

20%

33%

 

 

 

BT-13

BT-33

BT-14

BT-34

BT-17

BT-37

BJ-13

BJ-33

 

BJ-14

BJ-34

BJ-17

BJ-37

MECHANICAL

 

 

 

 

 

 

 

 

 

Tensile Strength

 

 

Ultimate Elongation

 

 

Flexural Modulus

 of Elasticity

 

Flexural Strength

 

 

Izod Impact Strength

  1/8” Thickness        

   Notched

   @ 73F (23C)

 

 

Rockwell Hardness

 

 

Compressive Strength

   at Yield

 

 

 

D-638

 

 

D-638

 

 

D-790

 

 

D-790

 

 

 

 

D-256

 

 

 

 

D-785

 

 

 

D-695

 

 

 

 

 

 

Psi

Mpa

 

%

 

 

psi

MPa

 

Psi

MPa

 

 

 

ftlb/in

J/m

 

 

 

M Scale

R Scale

 

 

Psi

Mpa

 

 

13,500

93.1

 

3-4

 

 

600,000

4137

 

18,000

124

 

 

 

2.2

117

 

 

 

78

118

 

 

14,000

96.4

 

15,000

103

 

3-4

 

 

750,000

5171

 

22,000

152

 

 

 

2.4

128

 

 

 

82

118

 

 

17,000

117

 

 

 

 

 

20,500

141

 

3-4

 

 

950,000

6550

 

30,000

207

 

 

 

2.7

144

 

 

 

87

120

 

 

25,000

172

 

12,500

86.2

 

3-4

 

 

500,000

3448

 

15,600

108

 

 

 

2.8

149

 

 

 

76

112

 

 

15,000

103

 

14,500

100

 

3-4

 

 

600,000

4137

 

19,000

131

 

 

 

3.3

176

 

 

 

79

115

 

 

18,000

124

 

19,500

134

 

3-4

 

 

850,000

5861

 

27,000

179

 

 

 

4.0

213

 

 

 

83

118

 

 

21,000

145

THERMAL

 

 

 

 

 

 

 

 

 

Melting Range

 

Heat Deflection

  Temperature

   @264 psi

   @1.82 MPa

 

   @66 psi

   @0.45 MPa

 

D-789

 

 

 

D-648

 

 

D-648

 

F

C

 

 

F

C

 

F

C

 

410-430

210-221

 

 

370

188

 

390

199

 

410-430

210-221

 

 

385

196

 

400

204

 

410-430

210-221

 

 

415

213

 

425

218

 

410-430

210-221

 

 

370

188

 

390

199

 

410-430

210-221

 

 

385

196

 

400

204

 

410-430

210-221

 

 

415

213

 

425

218

MISCELLANEOUS

 

 

 

 

 

 

 

 

 

Flammability

 

 

Moisture Absorption

  24 Hour Immersion

 

 

Specific Gravity

 

 

Mold Shrinkage

 

UL-94

 

 

 

D-570

 

 

D-792

 

 

D-955

 

-

 

 

 

%

 

 

-

 

 

%

 

 

94 HB

 

 

 

0.9

 

 

1.17-1.19

 

 

0.6-0.9

 

94 HB

 

 

 

0.8

 

 

1.24-1.26

 

 

0.4-0.7

 

94 HB

 

 

 

0.7

 

 

1.33-1.35

 

 

0.2-0.5

 

94 HB

 

 

 

0.9

 

 

1.16-1.18

 

 

0.6-0.9

 

94 HB

 

 

 

0.8

 

 

1.22-1.24

 

 

0.4-0.7

 

94 HB

 

 

 

0.7

 

 

1.31-1.33

 

 

0.2-0.5

 

 

Impact Modified and Mineral filled

 

PROPERTIES

 

 

ASTM

TEST

METHOD

 

 

UNITS

 

GENERAL PURPOSE

 

IMPACT

MODIFIED

ULTRA

HIGH

IMPACT

 

MINERAL

FILLED

GLASS

REINFORCED

MINERAL

FILLED

 

 

 

 

 

 

40%

40%

 

 

 

BS-10

BS-30

BI-10

BI-30

BD-10

BD-30

BH-18

BH-38

        BL-18

        BL-38           

MECHANICAL

 

 

 

 

 

 

 

 

Tensile Strength

 

 

Ultimate Elongation

 

 

Flexural Modulus

 of Elasticity

 

Flexural Strength

 

 

Izod Impact Strength

  1/8” Thickness        

   Notched

   @ 73F (23C)

 

 

Rockwell Hardness

 

 

Compressive Strength

   at Yield

 

 

 

D-638

 

 

D-638

 

 

D-790

 

 

D-790

 

 

 

 

D-256

 

 

 

 

D-785

 

 

 

D-695

 

 

 

 

 

 

psi

MPa

 

%

 

 

psi

MPa

 

psi

MPa

 

 

 

ftlb/in

J/m

 

 

 

M Scale

R Scale

 

 

psi

MPa

 

 

11,000

75.8

 

60

 

 

390,000

2689

 

15,000

103

 

 

 

1.1

59

 

 

 

78

118

 

 

9,000

62

 

 

8,000

55.2

 

90

 

 

250,000

1724

 

11,000

75.8

 

 

 

3.5

187

 

 

 

72

114

 

 

8,000

55

 

 

7,000

48.3

 

70

 

 

230,000

1586

 

9,800

67

 

 

 

18

960

 

 

 

70

112

 

 

6,500

45

 

12,500

86.2

 

10-15

 

 

750,000

5171

 

18,000

124

 

 

 

0.75

40

 

 

 

90

121

 

 

23,000

159

 

19,800

137

 

2-3

 

 

1,100,000

7585

 

27,000

186

 

 

 

0.85

45

 

 

 

95

122

 

 

27,000

186

 

 

 

THERMAL

 

 

 

 

 

 

 

 

Melting Range

 

Heat Deflection

  Temperature

   @264 psi

   @1.82 MPa

 

   @66 psi

   @0.45 MPa

 

D-789

 

 

 

D-648

 

 

D-648

 

F

C

 

 

F

C

 

F

C

 

420-440

216-227

 

 

147

64

 

360

182

 

 

410-430

210-221

 

 

140

60

 

350

177

 

400-420

204-216

 

 

128

53

 

340

171

 

420-440

216-227

 

 

290

143

 

360

182

 

420-440

216-227

 

 

400

204

 

420

216

MISCELLANEOUS

 

 

 

 

 

 

 

 

Flammability

 

 

Moisture Absorption

  24 Hour Immersion

 

 

Specific Gravity

 

 

Mold Shrinkage

 

UL-94

 

 

 

D-570

 

 

D-792

 

 

D-955

 

-

 

 

 

%

 

 

-

 

 

%

 

 

94 V-2

 

 

 

1.8

 

 

1.12-1.14

 

 

1.1-1.4

 

94 HB

 

 

 

1.6

 

 

1.07-1.09

 

 

1.1-1.4

 

94 HB

 

 

 

1.5

 

 

1.06-1.08

 

 

1.1-1.4

 

 

94HB

 

 

 

0.7

 

 

1.47-1.49

 

 

0.8-1.2

 

94HB

 

 

 

0.7

 

 

1.46-1.48

 

 

0.4-0.7