PROPERTIES |
ASTM TEST METHOD |
UNITS |
PET |
PBT |
||
|
Glass Reinforced |
Glass
Reinforced Mineral
Filled |
Impact Modified |
Glass
Reinforced Heat
Stabilized |
|||
|
|
|
|
33% |
40% |
|
30% |
|
|
|
|
WR-37 |
WL-38 |
HI-10 |
HR-36 |
|
MECHANICAL |
|
|
|
|
|
|
|
Tensile
Strength Flexural
Modulus of Elasticity Flexural
Strength Izod Impact
Strength 1/8” Thickness Notched @ 73F (23C) Rockwell
Hardness Compressive Strength
at Yield |
D-638 D-790 D-790 D-256 D-785 D-695 |
psi MPa psi MPa psi MPa ft-lb/in J/m M Scale R Scale psi MPa |
23,200 160 1,330,000 9200 34,800 240 1.8 96 112 121 33,800 233 |
18,000 124 1,210,000 8350 25,400 175 1.3 70 87 120 21,000 145 |
6,500 45 300,000 2100 11,600 80 2.0 107 78 116 12,000 83 |
20,300 140 1,240,000 8550 28,300 195 1.6 85 84 118 18,000 124 |
|
THERMAL |
|
|
|
|
|
|
|
Melting Range Heat
Deflection Temperature @264 psi @1.82 MPa @66 psi @0.45 MPa |
D-789 D-648 D-648 |
F C F C F C |
450-480 232-249 437 225 477 247 |
450-480 232-249 419 215 470 243 |
410-440 210-227 122 50 280 138 |
410-440 210-227 388 198 420 216 |
|
MISCELLANEOUS |
|
|
|
|
|
|
|
Flammability Moisture
Absorption 24 Hour Immersion Specific
Gravity Mold Shrinkage |
UL-94 D-570 D-792 D-955 |
- % - % |
94 HB 0.05 1.58 0.2 – 0.3 |
94 HB 0.05 1.60 0.2 – 0.3 |
94 HB 0.06 1.29 1.2 – 1.6 |
94 HB 0.04 1.54 0.5 – 0.8 |
|
TO THE BEST OF OUR
KNOWLEDGE, THE INFORMATION CONTAINED HEREIN IS ACCURATE. HOWEVER, NEITHER ADELL PLASTICS, INC. NOR
ANY OF ITS AFFILIATES ASSUMES ANY LIABILITY WHATSOEVER FOR THE ACCURACY OR
COMPLETENESS OF THE INFORMATION CONTAINED HEREIN. DETERMINATIONS OF THE SUITABILITY OF ANY INFORMATION OR
MATERIAL FOR THE USE CONTEMPLATED, THE MANNER OF USE, AND WHETHER THERE IS
ANY INFRINGEMENT OF PATENTS, IS THE SOLE RESPONSIBILITY OF THE USER. |