PROPERTIES
|
ASTM
TEST METHOD |
UNITS |
GENERAL PURPOSE |
PC ALLOY |
GLASS REINFORCED |
||
|
|
|
|
|
|
|
|
|
|
|
|
|
DS-10* |
YS-10 |
DR-12 |
DR-16 |
DR-18 |
MECHANICAL
|
|
|
|
|
10% |
30% |
40% |
|
Tensile
Strength Ultimate
Elongation Flexural
Modulus of Elasticity Flexural
Strength Izod
Impact Strength 1/8” Thickness Notched @ 73°F (23°C) Rockwell
Hardness |
D-638 D-638 D-790 D-790 D-256 D-785 |
psi MPa % psi MPa psi MPa ft-lb/in J/m M Scale |
10,000 69.0 130 340,000 2340 14,000 96.5 15 800 70 |
9,000 62.0 150 315,000 2170 11,300 77.9 14 747 70 |
11,500 79.3 5 520,000 3580 17,700 122 1.1 59 76 |
21,000 145 3 1,175,000 8100 29,700 205 2.8 149 92 |
24,000 165 3 1,450,000 10000 31,000 214 3.0 160 95 |
THERMAL |
|
|
|
|
|
|
|
|
Heat
Deflection Temperature @ 264 psi @ 1.82 MPa @ 66 psi @ 0.45 MPa |
D-648 D-648 |
°F °C °F °C |
270 132 280 138 |
253 123 280 138 |
275 135 285 141 |
293 145 305 152 |
300 149 305 152 |
MISCELLANEOUS |
|
|
|
|
|
|
|
|
Moisture
Absorption 24 Hour Immersion Specific
Gravity Mold
Shrinkage Melt
Index @ 300°C/1200 g |
D-570 D-792 D-955 D-1238 |
% % g/10 min |
0.25 1.20 0.6 9 – 11** |
.020 1.22 0.6 4 – 6** |
0.22 1.27 0.3 - |
0.17 1.44 0.2 - |
0.15 1.52 0.15 - |
* Available in lubricated and release grades
**
Other Melt Flow grades available
|
TO THE BEST OF OUR KNOWLEDGE, THE INFORMATION CONTAINED
HEREIN IS ACCURATE. HOWEVER, NEITHER
ADELL PLASTICS, INC. NOR ANY OF ITS AFFILIATES ASSUMES ANY LIABILITY
WHATSOEVER FOR THE ACCURACY OR COMPLETENESS OF THE INFORMATION CONTAINED
HEREIN. DETERMINATIONS OF THE
SUITABILITY OF ANY INFORMATION OR MATERIAL FOR THE USE CONTEMPLATED, THE
MANNER OF USE, AND WHETHER THERE IS ANY INFRINGEMENT OF PATENTS, IS THE SOLE RESPONSIBILITY
OF THE USER. |