Homopolymer Polypropylene Specification Sheet

PROPERTIES ASTM
TEST
METHOD		 UNITS GLASS REINFORCED MINERAL FILLED
GLASS REINFORCED
GLASS/MINERAL
CONTENT		 20% 30% 40% 30% 40%
PRODUCT ER-14 ER-17 ER-18 EL-16 EL-18
MECHANICAL
TENSILE
STRENGTH		 D-638 psi
MPa		 10,500
72.4		 13,000
89.6		 14,000
96.5		 7,000
48.3		 8,500
58.6
ULTIMATE
ELONGATION		 D-638 % 2-3 2-3 2-3 5-9 3-7
FLEXURAL
MODULUS
OF ELASTICITY		 D-790 psi
MPa		 630,000
4344		 850,000
5861		 980,000
6757		 700,000
4826		 800,000
5516
FLEXURAL
STRENGTH		 D-790 psi
MPa		 12,000
86.02		 20,000
138		 21,500
148		 9,500
65.5		 12,000
82.7
IZOD IMPACT
STRENGTH
1/8" THICKNESS
@73F		 D-256 ftlb/in
J/m		 1.4
75		 1.8
96		 2.1
112		 0.9
49.0		 1.3
69.4
IZOD IMPACT
STRENGTH
1/8" THICKNESS
@73F UNNOTCHED		 ftlb/in
J/m		 6
320		 8
427		 9
480		 6.0
320		 8.0
427
ROCKWELL
HARDNESS		 D-785 M Scale
R Scale		 58
110		 60
115		 60
115		 69
100		 70
102
GARDNER IMPACT D-695 in-lb.
J		 4
0.5		 3
0.3		 3
0.3		 4
0.5		 5
0.6

THERMAL
MELTING
RANGE		 D-789 F
C		 340-380
171-193		 340-380
171-193		 340-380
171-193		 340-380
171-193		 340-380
171-193
HEAT
DEFLECTION
TEMPERATURE
@264
@1.82 MPa

@66psi
@0.45 MPa

D-648


D-648		  

F
C

F
C

  

293
145

300
149

  

310
154

320
160

  

315
157

330
166

  

285
141

310
154

  

295
146

315
157

MISCELLANEOUS
FLAMMABILITY UL-94 94 HB 94 HB 94 HB 94 HB 94 HB
MOISTURE
ABSORPTION
24HR IMMERSION		 D-570 % 0.05 0.03 0.03 0.03 0.03
SPECIFIC
GRAVITY		 D-792 1.02-1.05 1.11-1.13 1.21-1.23 1.12-1.14 1.22-1.24
MOLD
SHRINKAGE		 D-955 % 0.4-0.7 0.2-0.5 0.2-0.5 0.3-0.7 0.2-0.5
PROPERTIES ASTM
TEST
METHOD		 UNITS CALCIUM
CARBONATE
FILLED		 TALC FILLED MICA REINFOCED
GLASS/MINERAL
CONTENT		 20% 30% 40% 20% 30% 40% 20% 20% 40%
PRODUCT EZ-14 EZ-16 EZ-18 EA-14 EA-16 EA-18 EQ-14 EQ-16 EQ-18
MECHANICAL
TENSILE
STRENGTH		 D-638 psi
MPa		 4,200
29.0		 3,700
25.5		 3,400
23.4		 5,100
35.2		 4,800
33.1		 4,600
31.7		 5,100
35.2		 4,900
33.8		 4,700
32.4
ULTIMATE
ELONGATION		 D-638 % 80 70 50 25 16 10 5-7 3-5 2-4
FLEXURAL
MODULUS
OF ELASTICITY		 D-790 psi
MPa		 250,000
1724		 275,000
1896		 310,000
2137		 380,000
2620		 430,000
2965		 480,000
3310		 450,000
3103		 580,000
4000		 750,000
5171
FLEXURAL
STRENGTH		 D-790 psi
MPa		 5,000
34.5		 5,200
35.8		 5,400
37.2		 6,800
46.9		 7,000
48.3		 7,400
51.0		 7,300
50.3		 7,500
51.7		 7,700
53.1
IZOD IMPACT
STRENGTH
1/8" THICKNESS
@73F		 D-256 ft-lb/in
J/m		 0.75
40.0		 0.65
34.7		 0.55
29.3		 0.5
26.7		 0.5
26.7		 0.45
24.0		 0.6
32.0		 0.55
29.3		 0.5
26.7
IZOD IMPACT
STRENGTH
1/8" THICKNESS
@73F UNNOTCHED		 ft-lb/in
J/m		 11.5
614		 10.0
534		 8.0
427		 6.2
331		 5.8
309		 5.0
267		 5.0
267		 4.5
240		 4.0
213
ROCKWELL
HARDNESS		 D-785 M Scale
R Scale		 50
78		 52
81		 54
85		 68
98		 69
100		 70
101		 62
90		 68
98		 72
104
GARDNER
IMPACT		 D-695 in-lb.
J		 30
3.4		 24
2.7		 15
1.7		 6
0.7		 5.5
0.6		 5
0.6		 5
0.6		 4
0.5		 3
0.3

THERMAL
MELTING
RANGE		 D-789 F
C		 340-380
171-193		 340-380
171-193		 340-380
171-193		 340-380
171-193		 340-380
171-193		 340-380
171-193		 340-380
171-193		 340-380
171-193		 340-380
171-193
HEAT
DEFLECTION
TEMPERATURE
@264
@1.82 MPa

@66psi
@0.45 MPa

D-648


D-648

F
C

F
C		  

140
60

210
99

  

150
66

220
104

  

158
70

232
111

  

165
74

245
118

  

170
77

255
124

  

175
79

270
132

  

175
79

260
127

  

185
85

270
132

  

195
91

285
141

MISCELLANEOUS
FLAMMABILITY UL-94 94 HB 94 HB 94 HB 94 HB 94 HB 94 HB 94 HB 94 HB 94 HB
MOISTURE
ABSORPTION
24HR IMMERSION		 D-570 % 0.03 0.04 0.04 0.03 0.04 0.04 0.02 0.03 0.04
SPECIFIC
GRAVITY		 D-792 1.04-1.05 1.13-1.14 1.23-1.25 1.03-1.05 1.12-1.14 1.22-1.25 1.03-1.05 1.12-1.15 1.22-1.25
MOLD
SHRINKAGE		 D-955 % 1.2-1.6 1.0-1.4 0.8-1.2 0.8-1.2 0.6-1.0 0.6-1.0 0.6-1.0 0.5-0.9 0.4-0.8