Copolymer Specs

PROPERTIES	ASTM TEST METHOD	UNITS	GLASS REINFORCED			CALCIUM CARBONATE FILLED
GLASS/MINERAL CONTENT			20%	30%	40%	20%
PRODUCT			RR-14	RR-17	RR-18	RZ-14
MECHANICAL
TENSILE STRENGTH	D-638	psi MPa	8,800 60.7	11,000 75.8	11,900 82.1	3,300 22.8
ULTIMATE ELONGATION	D-638	%	7-12	5-9	4-5	100+
FLEXURAL MODULUS OF ELASTICITY	D-790	psi MPa	480,000 3310	650,000 4482	740,000 5102	180,000 1241
FLEXURAL STRENGTH	D-790	psi MPa	10,600 73.1	15,000 103	16,000 110	4,800 33.1
IZOD IMPACT STRENGTH 1/8" THICKNESS @73F	D-256	ftlb/in J/m	1.7 90.7	2.2 117	2.5 133	1.5 80.0
IZOD IMPACT STRENGTH 1/8" THICKNESS @73F UNNOTCHED		ftlb/in J/m	8.0 427	10.0 534	11.0 587	22.0 1174
ROCKWELL HARDNESS	D-785	M Scale R Scale	53 87	57 105	58 110	45 66
GARDNER IMPACT	D-695	in-lb. J	8 0.9	7 0.8	6 0.7	120 13.6
THERMAL
MELTING RANGE	D-789	F C	300-340 149-171	300-340 149-171	300-340 149-171	300-340 149-171
HEAT DEFLECTION TEMPERATURE @264 @1.82 MPa @66psi @0.45 MPa	D-648 D-648	F C F C	280 138 295 146	295 146 310 154	300 149 315 157	120 49 170 77
MISCELLANEOUS
FLAMMABILITY	UL-94		94 HB	94 HB	94 HB
MOISTURE ABSORPTION 24HR IMMERSION	D-570	%	0.05	0.03	0.03	0.02
SPECIFIC GRAVITY	D-792		1.02-1.05	1.11-1.13	1.21-1.23	1.04-1.05
MOLD SHRINKAGE	D-955	%	0.4-0.7	0.2-0.5	0.2-0.5	1.0-1.4

PROPERTIES	ASTM TEST METHOD	UNITS	CALCIUM CARBONATE FILLED		TALC FILLED			MICA REINFOCED
GLASS/MINERAL CONTENT			30%	40%	20%	30%	40%	20%	20%	40%
PRODUCT			RZ-16	RZ-18	RA-14	RA-16	RA-18	RQ-14	RQ-16	RQ-18
MECHANICAL
TENSILE STRENGTH	D-638	psi MPa	3,100 21.4	2,800 19.3	4,100 28.3	3,900 26.9	3,700 25.5	3,800 26.2	4,100 28.3	4,500 31.0
ULTIMATE ELONGATION	D-638	%	100+	80	20	15	10	5-9	4-6	2-4
FLEXURAL MODULUS OF ELASTICITY	D-790	psi MPa	200,000 1379	230,000 1586	240,000 1655	270,000 1862	310,000 2137	250,000 1724	450,000 3103	690,000 4758
FLEXURAL STRENGTH	D-790	psi MPa	4,700 32.4	4,600 31.7	5,500 37.9	5,400 37.2	5,200 35.9	6,500 44.8	6,700 46.2	7,00 48.3
IZOD IMPACT STRENGTH 1/8" THICKNESS @73F	D-256	ft-lb/in J/m	1.2 64.0	0.9 48.0	1.0 53.4	0.9 48.0	0.7 37.3	1.5 80.0	1.2 64.0	0.8 42.7
IZOD IMPACT STRENGTH 1/8" THICKNESS @73F UNNOTCHED		ft-lb/in J/m	18 960	12 640	8.0 427	7.0 373	5.5 293	6.0 320	5.0 267	4.0 213
ROCKWELL HARDNESS	D-785	M Scale R Scale	47 68	49 71	48 74	49 76	50 79	60 85	66 94	70 100
GARDNER IMPACT	D-695	in-lb. J	100 11.3	80 9.0	30 3.4	20 2.3	10 1.1	15 1.7	12 1.4	10 1.1
THERMAL
MELTING RANGE	D-789	F C	300-340 149-171	300-340 149-171	300-340 149-171	300-340 149-171	300-340 149-171	300-340 149-171	300-340 149-171	300-340 149-171
HEAT DEFLECTION TEMPERATURE @264 @1.82 MPa @66psi @0.45 MPa	D-648 D-648	F C F C	130 54 185 85	140 60 200 93	140 60 235 113	150 66 250 121	160 71 270 132	160 71 255 124	200 93 272 133	230 110 285 141
MISCELLANEOUS
FLAMMABILITY	UL-94		94 HB		94 HB	94 HB	94 HB	94 HB	94 HB	94 HB
MOISTURE ABSORPTION 24HR IMMERSION	D-570	%	0.03	0.04	0.02	0.03	0.04	0.02	0.03	0.04
SPECIFIC GRAVITY	D-792		1.12-1.14	1.22-1.25	1.03-1.05	1.12-1.14	1.22-1.25	1.03-1.05	1.12-1.15	1.22-1.25
MOLD SHRINKAGE	D-955	%	0.9-1.3	0.8-1.2	0.8-1.2	0.7-1.1	0.6-1.0	0.6-1.0	1.5-0.9	0.4-0.8